1. After the organic modification of montmorillonite , the interplanar spacing of montmorillonite increased from 1 . 21nm to 1 . 78nm . up ( unsaturated polyester ) mmt ( montmorillonite ) nanocomposites were prepared by dispersing organically modified montmorillonite in prepromoted up resin and subsequently cross - linked using methyl ethyl ketone peroxide catalyst at several different clay concentrations
   將有機蒙脫土分散到不飽和聚酯中，加入引發(fā)劑(過氧化甲乙酮) 、促進劑(環(huán)烷酸鈷) ，使不飽和聚酯交聯(lián)制得納米復(fù)合材料。
2. The results show that ti2n ( 200 ) tropism interplanar is obtained when the ion beam energy is 875ev and the current is 60ma . the ti2n crystals embed in the films deposited at low temperature , while tin crystals are formed at high temperature . the analyses of component show that the tiny films are rich - nitrogen
   結(jié)果表明：在能量為875ev 、束流為60ma時獲得取向較好的ti _ 2n ( 200 )晶面；低溫沉積的薄膜的主晶相為ti _ 2n ，高溫沉積時為tin ；成分分析表明tin _ y薄膜是富氮的。
3. The content of pema affects on interplanar distance of pe / mmt composite . the content of pema increases as the interplanar distance , barrier properties and melting point of composites increased , when the critical content of pema ( wpema = 30 % ) could get exfoliated composites . the interlayer spacing of pe / mmt composites depends on content of mmt , but not the content of mmt increases as the interlayer spacing increases
   同時用x射線衍射（ xrd ）衍射實驗、紅外光譜( ir )實驗、差熱分析試驗（ dta ） 、力學(xué)性能測試等手段，研究了采用不同的相容劑改善聚乙烯與蒙脫土之間的相容性的情況；相容劑的用量對聚乙烯/蒙脫土復(fù)合材料層間距、性能的影響；蒙脫土的含量對pe / mmt對復(fù)合體系的層間距影響；以及工藝條件對復(fù)合體系的層間距和性能的影響。
4. The results showed that the interplanar spacing d values and relative x - ray diffraction intensity of the mixed lb films change with the ratio of ba / sa in a step - and w - shaped curve respectively , which indicates that only three kinds of longitudinal periodic structures can form in the mixed multilayer lb films of all ratios and each microstructure can be maintained in a certain ratio range . furthermore the mixed system always goes through a process of the longitudinal regularity decreasing when the ratio of ba / sa is out of the intermediate ratio range ( ba / sa : 1 / 5 ~ 1 / 1 )
   結(jié)果發(fā)現(xiàn)，對于sa ba混合膜，分相小而均勻，不出現(xiàn)單獨的衍射周期；隨比例不同，縱向面間距出現(xiàn)臺階效應(yīng)，表明存在3類結(jié)構(gòu)，其中在較大比例范圍內(nèi)出現(xiàn)了長短鏈交錯的結(jié)構(gòu)，這種結(jié)構(gòu)具有高的穩(wěn)定性和有序性；在ba較多的混合膜中，在脂鏈層間出現(xiàn)空洞結(jié)構(gòu)，可以用來構(gòu)造特殊的納米結(jié)構(gòu)。